| Título : | ZrO2 addition in mould powders: effect on horizontal heat transfer rate and sen erosion rate |
| Título en inglés: | ZrO2 addition in mould powders: effect on horizontal heat transfer rate and sen erosion rate |
| Autor : | Pereira, Márcia Maria da Silva Monteiro Lima, Marco Túlio Dias Berlini Filho, Carlos Mendes, Sebastião Garcia Ferreira, Gérson Tolentino Jung, Detlef Klug, Jeferson Leandro |
| Palabras clave : | Lingotamento contínuo;Pó fluxante;Erosão da válvula submersa;Trinca longitudinal |
| Fecha de publicación : | 2015 |
| Editorial : | ABM Week - https://abmproceedings.com.br/; Editora Blucher |
| Citación : | PEREIRA, Márcia Maria da Silva Monteiro; LIMA, Marco Túlio Dias; BERLINI FILHO, Carlos; MENDES, Sebastião Garcia; FERREIRA, Gérson Tolentino; JUNG, Detlef; KLUG, Jeferson Leandro. ZrO2 addition in mould powders: effect on horizontal heat transfer rate and sen erosion rate. In: SEMINÁRIO DE ACIARIA - INTERNACIONAL, 46º., Rio de Janeiro, v. 46, n. 46, p. 281-288. 2015. |
| Resumen en portugués brasileño: | Durante o lingotamento contínuo de aço, partículas de ZrO2 adicionadas na escória de molde facilitam a nucleação heterogênea de cristais devido à sua limitada solubilidade. A adição de ZrO2 promove a cristalização da fase cuspidina, o que auxilia na redução da transferência horizontal de calor no molde, amenizando desta forma o problema das trincas longitudinais. Outro benefício da adição de ZrO2 em pós fluxantes é reduzir a taxa de desgaste da válvula submersa (SEN) na interface metal/escória; a erosão da SEN é um problema sério. Através de testes de laboratório e de testes industriais concluiu-se que a adição de ZrO2 em pós fluxantes reduz a taxa de transferência de calor horizontal no molde durante o lingotamento contínuo de aço, considerando os dois tipos de pós fluxantes que foram analisados no presente trabalho. Além disso, observou-se que a adição de ZrO2 reduz a taxa de desgaste da válvula submersa na interface metal/escória. |
| Abstract: | During continuous casting of steel, it is accepted that ZrO2 particles in the mould slag act as heterogeneous nucleation sites due to its limited solubility. ZrO2 addition promotes crystallisation of cuspidine and consequently reduces horizontal heat transfer, alleviating in this way problems associated with longitudinal cracking. Another benefit when adding ZrO2 in mould powders is to reduce erosion of SENs at the slag/metal interface; SEN erosion is a serious problem. Through laboratory tests and industrials tests it was concluded that ZrO2 addition in mould powders can reduce horizontal heat transfer rate for the mould during continuous casting of steel, considering two particular mould powders which were studied in the present work. Besides, it was observed that ZrO2 addition reduces erosion of SEN at the slag/metal interface. |
| URI : | http://www.repositorio.ufc.br/handle/riufc/58036 |
| ISSN : | 1982-9345(dentro do artigo) 2594-5300 (https://abmproceedings.com.br) |
| Aparece en las colecciones: | DEMM - Trabalhos apresentados em eventos |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 2015_eve_mdasmpereira.pdf | 1,11 MB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.