Avaliação microscópica, estudo histoquímico e análise de propriedades tensiométricas da pele de tilápia do Nilo

Abstract

OBJECTIVE: To characterize the Nile tilapia skin, a possible source of biomaterial for grafting, from their physical (tensile strength) and histomorphological characteristics, and from collagen classification. METHODS: Samples of Nile tilapia skin were used and, for microtensile tests (by Instron® universal testing machine), were subjected to immersion in glycerol solutions of increasing concentration. Part of the samples was fixed in neutral formalin 10%, processed and prepared using routine staining with hematoxylin and eosin into tissue slides, for further histological and histochemical analysis. All steps were also played in human skin, donated by plastic surgeries, for comparative effects. RESULTS: The morphology of Nile tilapia skin presented similarities with human skin, showing the deep dermis formed by thick organized collagen fibers, on parallel/horizontal and transversal/vertical arrangement. The tilapia skin also presented a larger composition of type I collagen, compared with human skin (p=0.015). On traction tests, the load average supported by tilapia skin was 43.9±26.2 N, while the traction extensile had mean values of 4.44±1.045cm. CONCLUSION: The tilapia skin has microscopic characteristics, similar to the morphological structure of human skin, and high resistance and tensile extension at break, which supports its possible application as biomaterial. The dermis of this skin is composed by organized bundles of dense collagen fibers, predominantly type I ones, which brings considerable importance for its clinical use.