| Título : | Evaluation of the anticorrosive properties of environmental friendly inorganic corrosion inhibitors pigments |
| Autor : | Leite, Adriana de Oliveira Sousa Araújo, Walney Silva Margarit-Mattos, Isabel Cristina Pereira Correia, Adriana Nunes Lima Neto, Pedro de |
| Palabras clave : | Steel;Corrosion;Anticorrosive pigments;Mass loss;Electrochemical tests;Surface analysis;Aço;Corrosão;Pigmentos anticorrosivos;Perda de massa;Testes eletroquimicos;Análise de superfície |
| Fecha de publicación : | 2005 |
| Editorial : | Journal of the Brazilian Chemical Society |
| Citación : | LEITE, Adriana de Oliveira Sousa; ARAÚJO, Walney Silva; MARGARIT, Isabel Cristina Pereira; CORREIA, Adriana Nunes; LIMA NETO, Pedro de. Evaluation of the anticorrosive properties of environmental friendly inorganic corrosion inhibitors pigments. Journal of the Brazilian Chemical Society, São Paulo, v.16, n. 4, p. 756-762, 2005 |
| Resumen en portugués brasileño: | Neste trabalho foram estudadas as propriedades anticorrosivas de cinco pigmentos inorgânicos comerciais considerados ecologicamente corretos: fosfato de zinco (ZP), molibdato de zinco (ZM), molibdato de zinco e cálcio (ZCM), fosforomolibdato de zinco (ZPM) e fosforomolibdato de zinco e cálcio (ZCPM). Amostras de aço AISI 1010 foram imersas em solução aquosa de NaCl 10-2 mol dm-3 saturada com um dos pigmentos, seguido de medidas de perda de massa, monitoramento do potencial de circuito aberto com o tempo de imersão e polarização linear potenciodinâmica a 1 mV s-1. Os produtos de corrosão foram caracterizados por Microscopia Eletrônica de Varredura, Energia Dispersiva da raios-X e Difração de raios-X. Todos os pigmentos inibiram a corrosão do aço. Os filmes formados na superfície protegem o aço contra corrosão. Os resultados sugerem efeito sinérgico entre os compostos de fosfato e molibdato nos pigmentos a base de fosforomolibdato. Os pigmentos ZMP e ZCPM diminuíram a taxa de corrosão por um fator de 2,15 e 3,50, respectivamente. |
| Abstract: | Anticorrosive properties of the following environmental friendly inorganic pigments were evaluated: zinc phosphate (ZP), zinc molybdate (ZM), zinc calcium molybdate (ZCM), zinc phosphomolybdate (ZPM) and zinc calcium phosphomolybdate (ZCPM). AISI 1010 steel samples were immersed in 10-2 mol dm-3 NaCl aqueous solution saturated with one of the pigments, followed by mass loss measurements, by monitoring the open circuit potential with immersion time and by potentiodynamic linear polarization at 1 mV s-1. The corrosion products on the steel surface were characterized by Scanning Electron Microscopy, Energy Dispersive X-ray and X-rays Diffraction analyses. All the pigments inhibited the corrosion of steel. The films formed on the steel surface protect the substrate against corrosion. The results suggest a synergic effect of phosphate and molybdate compounds in the phosphomolybdate-based pigments, improving the corrosion resistance of steel. The ZMP and ZCPM decreased the corrosion rate by a factor of 2.15 and 3.50, respectively. |
| URI : | http://www.repositorio.ufc.br/handle/riufc/72374 |
| ISSN : | 0103-5053 |
| Aparece en las colecciones: | DEME - Artigos publicados em revista científica |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 2005_art_plimaneto.pdf | 555,26 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.