| Título : | Characterisation of electrodeposited and heat-treated Ni−Mo−P coatings |
| Autor : | Melo, Régis Lopes Casciano, Paulo Naftali da Silva Correia, Adriana Nunes Lima Neto, Pedro de |
| Palabras clave : | Ni−Mo−P;Electrodeposition;Amorphous;Corrosion;Hardness;Eletrodeposição;Amorfo;Corrosão;Dureza |
| Fecha de publicación : | 2012 |
| Editorial : | Journal of the Brazilian Chemical Society |
| Citación : | MELO, Régis Lopes; CASCIANO, Paulo Naftali Da Silva; CORREIA, Adriana Nunes; LIMA NETO, Pedro de. Characterisation of electrodeposited and heat-treated Ni−Mo−P coatings. Journal of the Brazilian Chemical Society, [s.l.], v.. 23, n. 2, p. 328-334, 2012. |
| Resumen en portugués brasileño: | A eletrodeposição e as propriedades de dureza e resistência à corrosão de eletrodepósitos de Ni−Mo−P foram estudadas. A caracterização das camadas foi feita por microscopia eletrônica de varredura, difração de raios X e energia dispersiva de raios X. Os ensaios de corrosão foram feitos à temperatura ambiente em NaCl 10-1 mol dm-3 e por polarização linear potenciodinâmica. Camadas amorfas de Ni−Mo−P foram obtidas e a composição destas mostrou ser dependente da composição do banho, da densidade de corrente aplicada e da temperatura do banho. A dureza das camadas de Ni−Mo−P mostrou ser dependente dos teores de Mo e P e que a ausência de trincas é um requerimento necessário para obter eletrodepósitos de Ni−Mo−P com boas propriedades de dureza. A dureza das camadas tratadas termicamente aumentou com a temperatura de tratamento térmico devido à precipitação das fases Ni, Ni3P e NiMo durante o tratamento térmico. A resistência à corrosão dos eletrodepósitos de Ni−Mo−P aumentou com o teor de P na camada. A camada Ni78Mo10P12 apresentou os maiores valores de dureza a a maior resistência à corrosão. A adição de P mostrou ser benéfica para as propriedades de dureza e resistência à corrosão de eletrodepósitos de Ni−Mo. |
| Abstract: | The electrodeposition, hardness and corrosion resistance properties of Ni−Mo−P coatings were investigated. Characterisations of the electrodeposited coatings were carried out using scanning electron microscopy, X-ray diffraction and energy dispersive X-ray analysis techniques. Corrosion tests were performed at room temperature in 10-1 mol dm-3 NaCl solutions and by potentiodynamic linear polarisation. Amorphous Ni−Mo−P coatings were successfully obtained by electrodeposition using direct current. The coating composition showed to be dependent on the bath composition, current density and bath temperature. Both P and Mo contents contribute for the hardness properties of the Ni−Mo−P coatings and the absence of cracks is a requirement to produce electrodeposited Ni−Mo−P coatings with good hardness properties. The hardness values increase with heat-treatment temperature due to the precipitation of Ni, Ni3P and NiMo phases during the heat treatment. The corrosion resistance of the electrodeposited Ni−Mo−P amorphous coatings increases with P content in the layer. Among the electrodeposited Ni−Mo−P amorphous coatings, Ni78Mo10P12 presented the best hardness and corrosion-resistance properties. The results showed that the addition of P is beneficial for the hardness and corrosion resistance properties of the Ni−Mo-based coatings |
| URI : | http://www.repositorio.ufc.br/handle/riufc/72292 |
| ISSN : | 1678-4790 |
| Aparece en las colecciones: | DEME - Artigos publicados em revista científica |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 2012_art_plimaneto1.pdf | 875,95 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.