| Título : | Textural analysis through thickness of API X70 steel after hot rolling and post heat treatment |
| Título en inglés: | Textural analysis through thickness of API X70 steel after hot rolling and post heat treatment |
| Autor : | Masoumi, Mohammad Abreu, Hamilton Ferreira Gomes de |
| Palabras clave : | Aço API-X70;Laminação a quente;EBSD;Difração de eletrons |
| Fecha de publicación : | 2015 |
| Editorial : | ABM Week - https://abmproceedings.com.br/; Editora Blucher |
| Citación : | MASOUMI, Mohammad; ABREU, Hamilton Ferreira Gomes de. Textural analysis through thickness of API X70 steel after hot rolling and post heat treatment. In: SEMINÁRIO DE LAMINAÇÃO – PROCESSOS E PRODUTOS LAMINADOS E REVESTIDOS, part of the ABM WEEK., 52º., 17 a 21 ago. 2015, Rio de Janeiro, RJ, Brazil. Anais[...], Rio de Janeiro,v.52, n.52, p. 89-98, 2015. |
| Resumen en portugués brasileño: | No presente estudo, as amostras de aço de dutos API 5L X70 foram deformadas por laminação a quente resfriadas ao ar ou temperadas em água e, posteriormente, revenidas em diferentes temperaturas. A difração de raios-X (XRD) e a técnica de difração de elétron retroespalhado (EBSD) foram usadas para analisar a evolução da textura do estado inicial para o estado de laminação e têmpera na espessura média e próximo ao plano da superfície de todas as amostras. Os resultados mostraram que a região de espessura média é mais rica em grãos orientados {100} // ND, conhecidos como mais suscetíveis à formação e crescimento de fissuras. Amostra deformada a quente mostrou grãos de recristalização dinâmica, enquanto a amostra temperada a 700 ° C evidenciou recuperação e crescimento de grão. |
| Abstract: | In the present study, API 5L X70 pipeline steel samples were deformed by hot-rolling cooled in air or quenched in water and subsequently tempered at different temperatures. X-ray diffraction (XRD) and electron backscatter diffraction (EBSD) technique were used to analyze the texture evolution from the initiate state to rolling and tempering state at mid-thickness and near surface plane of all samples. The results showed that the mid-thickness region is richer in {100}//ND oriented grains known as more susceptible to crack formation and growth through. Hot deformed specimen showed dynamic recrystallization grains while quench tempered sample at 700°C evidenced recovery and grain growth. |
| URI : | http://www.repositorio.ufc.br/handle/riufc/57863 |
| ISSN : | 1983-4764 2594-5297 |
| Aparece en las colecciones: | DEMM - Trabalhos apresentados em eventos |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 2015_eve_mmasoumi.pdf | 1,38 MB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.