| Título: | Corrosion study of electrodeposited Zn and Zn-Co coatings in chloride medium |
| Autor(es): | Lima Neto, Pedro de Correia, Adriana Nunes Colares, Regilany Paulo Araújo, Walney Silva |
| Palavras-chave: | Zn;Zn-Co;Electrodeposition;Corrosion;Electrochemical techniques |
| Data do documento: | 2007 |
| Instituição/Editor/Publicador: | Journal of the Brazilian Chemical Society |
| Citação: | LIMA-NETO, Pedro de et al. Corrosion study of electrodeposited Zn and Zn-Co coatings in chloride medium. Journal of the Brazilian Chemical Society, [s. l.], v. 18, n. 6, p. 1164-1175, 2007. |
| Resumo: | A corrosão de eletrodepósitos de Zn e Zn-Co em solução aquosa de NaCl 0.1 mol dm-3 foi investigada usando as técnicas de microscopia eletrônica de varredura (SEM), energia dispersiva de raios-X (EDX), dissolução anódica sob controle galvanostático (GES), impedância eletroquímica (EIS) e medidas de potencial de circuito aberto (Eoc). Todos os eletrodepósitos foram feitos sobre aço carbono. Fases intermetálicas foram identificadas nas camadas de ZnCo com teor de Co superior a 1 at.%. Os resultados de GES, SEM e EDX mostraram que o mecanismo de corrosão das camadas de Zn-Co com mais alto teor de Co está relacionado ao surgimento de trincas devido à dissolução de fases intermetálicas ricas em Zn, enquanto que a corrosão das camadas de Zn e Zn-1Co foi caracterizada pela dissolução destas. Os produtos de corrosão identificados foram os mesmos em todas as camadas testadas, os quais atuaram como barreira, mas não foram capazes de prevenir o processo corrosivo. A melhor resistência à corrosão das camadas de Zn-Co obtidas a partir do banho não aditivado, em comparação à camada de Zn-1Co obtida do banho aditivado, é devido ao elevado teor de Co que promove um enobrecimento da camada. Todas as camadas de Zn-Co apresentaram resistência à corrosão superior às camadas de Zn. A camada Zn-18Co apresentou o melhor desempenho anticorrosivo com uma durabilidade 3 vezes superior a camada de Zn. |
| Abstract: | The corrosion behavior of electrodeposited Zn and Zn-Co coatings in 0.1 mol dm-3 NaCl aqueous solutions was investigated using scanning electron microscopy (SEM), energy dispersive X-ray (EDAX), galvanostatic electrochemical stripping (GES), electrochemical impedance spectroscopy (EIS) techniques and open circuit measurements (Eoc). All coatings were electrodeposited on mild steel. Using GES it was possible to identify Zn-Co intermetallic phases in the coatings with Co content higher than 1 at.%. The GES, SEM and EDX results revealed that the corrosion mechanism of the Zn-Co layers with high Co content is related to the appearance of cracks due to the dissolution of the γ Zn-rich phases, while the corrosion of the Zn and Zn- 1Co layers was characterized by dissolution of the coatings. The Zn and Zn-Co coatings were found to contain the same insoluble corrosion products, which act as a corrosion barrier that delays but does not prevent corrosion. The better corrosion resistance of the Zn-Co coatings obtained in the bath without additive, in comparison with Zn-1Co obtained in the bath containing additive is due to the high Co content which leads to an ennoblement of the coating. All Zn-Co electrodeposits showed greater corrosion resistance than the Zn electrodeposits. The Zn-18Co layer showed the best corrosion resistance, with a lifetime about three times longer than that of the Zn layer. |
| URI: | http://www.repositorio.ufc.br/handle/riufc/68305 |
| ISSN: | 1678-4790 |
| Aparece nas coleções: | DEMM - Artigos publicados em revista científica |
Arquivos associados a este item:
| Arquivo | Descrição | Tamanho | Formato | |
|---|---|---|---|---|
| 2007_art_plimaneto.pdf | 592,18 kB | Adobe PDF | Visualizar/Abrir |
Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.