Desenvolvimento do compósito magneto-dielétrico de Y3Fe5O12/CaTiO3 para uso em dispositivos que operem micro-ondas

Abstract

With the development of wireless technology, many electronic devices require high integration and materials with multifunctional properties. In such a case, magneto-dielectric composites have attracted much attention because they have both magnetic and dielectric properties. In this sense, research on composites is employed to search for new materials. The calcium titanate and yttrium iron garnet possess excellent dielectric properties and ferrimagnetic, respectively. This paper presents the preparation of ferrimagnetic composite, comprising the steps Y3Fe5O12 (YIG) and CaTiO3 (CTO) by the solid state synthetic route with the use of high energy mechanical grinding. The phases of the ceramics were sintered at 1200 ° C for 5 h. The X-ray diffraction, Raman and Mössbauer Spectroscopy were used to elucidade structural properties of the composites. The morphological characteristics of the samples were elucidated by Scanning Electron Microscopy and supported by Pycnometry to analyze the densification of the material. Furthermore, experiments to evaluate the electrical and magnetic behavior of composites in the range of radiofrequency and microwave were performed and finally an appropriate technological application was suggested. The results obtained by X-Ray Diffraction and Raman spectroscopy confirm that the synthesis of YIG was successfully obtained. The structural characterization of pure and composite samples was performed successfully and the formation of ionic phase in composites YIG-CTO was found, being in the same family of oxide in which the CTO is inserted. Qualitative analysis of the Mössbauer spectra showed good agreement with the results reported by x-ray diffraction. The dielectric permittivity composites showed almost constant in the range of 50 MHz to 1.5 GHz. Evaluating the increasing and decreasing in mass concentration of CTO and YIG, respectively and it was realized that the values of εr increased. Two profiles was noticed in the compositional series, it can be inferred that the possibility of the reaction of YIG and CTO products may be interfering with the proper measurements.