Title in Portuguese: Análise de textura em aços maraging 300 solubilizado em altas temperaturas
Title: Analysis of maraging 300 steel texture solution annealing in high temperatures
Author: Vieira, Regina Coeli Araújo
Muniz, Letícia Rabelo
Silva, Marcelo José Gomes da
Abreu, Hamilton Ferreira Gomes de
Keywords: Maraging 300
Solubilização
Textura Cristalográfica
Issue Date: 2018
Publisher: ABM Week - https://abmproceedings.com.br/; Editora Blucher
Citation: VIEIRA, Regina Coeli Araújo; MUNIZ, Letícia Rabelo; SILVA, Marcelo José Gomes da; ABREU, Hamilton Ferreira Gomes de. Análise de textura em aços maraging 300 solubilizado em altas temperaturas. In: CONGRESSO ANUAL DA ABM, 73º., 02 a 04 out. 2018, São Paulo, SP, Brasil. Anais[...]. São Paulo, v. 73, n.73, p. 1360-1371, 2018.
Abstract in Portuguese: Os aços Maraging são aços de ultra-alta resistência com aplicações, desde vasos de alta pressão de operação em processos críticos até equipamentos esportivos. Atualmente, os aços Maraging com 18% de Ni são os mais utilizados. Eles podem ser fornecidos nas classes 200, 250, 300 e 350. O presente estudo utilizou o aço Maraging 300, que foi tratado termicamente em temperaturas de solubilização acima da convencional, com o objetivo de melhorar a tenacidade à fratura sem perdas significativas da resistência mecânica. A solubilização em temperaturas acima da recomendada pelos fabricantes (820°C) resultou em um crescimento do grão austenítico, que se tornou muito acentuado acima de 1000°C. O aço Maraging é um material anisotrópico, portanto, é importante analisar a orientação cristalográfica do material. Para isso, foi realizado Difração de Raio-X nas amostras. Foi observado que a textura de Cubo Girado persiste, após a solubilização, em diferentes intensidades. Já a fibra gama não continua após os tratamentos térmicos de solubilização.
Abstract: Maraging steels are ultra-high resistance steels with applications, from vessels of high pressure of operation in critical processes to sportive equipment. currently, maraging steels with 18% of ni are the most used. They can be provided in classes 200, 250, 300 and 350. This study used steel maraging 300, that was treated thermically in upper solubility temperatures of the conventional, with the aim of improving tenacity to the fracture without losses significance of mechanical resistance. The solution annealing in temperatures above recommended by the manufacturers (820 ° c) results in grain growth austenic, which has been very accented above 1000 ° c. maraging steel, when deformed, develops a texture that is enough reduced by solution annealing, which destroys the rolling texture. Analysis of the crystallographic orientation of the material. For that, x-ray difference was made in the samples. Watched that the texture of turned cube persists, after solution annealing, in different intensities. Fiber fiber does not continue after the thermal treatments of solution annealing.".
URI: http://www.repositorio.ufc.br/handle/riufc/57866
metadata.dc.type: Artigo de Evento
ISSN: 2594-5327
metadata.dc.identifier.other: DOI 10.5151/1516-392X-31640
Appears in Collections:DEMM - Trabalhos apresentados em eventos

Files in This Item:
File Description SizeFormat 
2018_eve_rcavieira.pdf897,95 kBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.