Título: Microstructural, magnetic and mechanical property changes in an AISI 444 stainless steel aged in the 560 °C to 800 °C range
Autor(es): Tavares, Sérgio Souto Maior
Souza, J. A. de
Herculano, Luís Flávio Gaspar
Abreu, Hamilton Ferreira Gomes de
Souza Júnior, Carlos Marley de
Palavras-chave: Ciência dos materiais
Aço inoxidável ferrítico
Aço - Propriedades
Aging
Ferritic stainless steel
Data do documento: Fev-2008
Editor: Materials Characterization
Citação: TAVARES, S. S. M. ; SOUZA, J. A. ; HERCULANO, L. F. G. ; ABREU, H. F. G. ; SOUZA JR, C. M. (2008)
Abstract: AISI 444 steel is an 18Cr–2Mo ferritic stainless steel, containing Ti and Nb as stabilizing elements. The effects of aging in the 560–800 °C range on the microstructure, mechanical and magnetic properties were investigated. The material was not susceptible to sigma phase formation until 100 h of exposure. Slight hardening at 560 °C and progressive softening in the 650 °C–800 °C range were observed. At these temperatures, Mo-rich phases such as Fe2Mo and FeMoSi precipitate. The increase of particle sizes with the increase of temperature above 650 °C is responsible for the decrease of hardness. Precipitation of the Mo-rich phases increases the coercive force.
Descrição: TAVARES, S. S. M. et al. Microstructural, magnetic and mechanical property changes in an AISI 444 stainless steel aged in the 560 °C to 800 °C range. Materials Characterization, v. 59, n. 2, p. 112-116. 2008.
URI: http://www.repositorio.ufc.br/handle/riufc/28801
ISSN: 1044-5803
Aparece nas coleções:DEMM - Artigos publicados em revista científica

Arquivos associados a este item:
Arquivo Descrição TamanhoFormato 
2008_art_hfgabreu_Microstructural, magnetic and mechanical.pdf1,04 MBAdobe PDFVisualizar/Abrir


Os itens no repositório estão protegidos por copyright, com todos os direitos reservados, salvo quando é indicado o contrário.